IOP PUBLISHING

JOURNAL OF PHYSICS: CONDENSED MATTER

J. Phys.: Condens. Matter 21 (2009) 314015 (7pp)

doi:10.1088/0953-8984/21/31/314015

Spatially resolved, energy-filtered imaging of core level and valence band photoemission of highly p and n doped silicon patterns N Barrett1 , L F Zagonel1 , O Renault2 and A Bailly2 1 2

CEA DSM/IRAMIS/SPCSI, CEA Saclay, 91191 Gif sur Yvette, France CEA-LETI, MINATEC, 17 rue des Martyrs, 38054 Grenoble Cedex 9, France

E-mail: [email protected]

Received 19 December 2008 Published 7 July 2009 Online at stacks.iop.org/JPhysCM/21/314015 Abstract An accurate description of spatial variations in the energy levels of patterned semiconductor substrates on the micron and sub-micron scale as a function of local doping is an important technological challenge for the microelectronics industry. Spatially resolved surface analysis by photoelectron spectromicroscopy can provide an invaluable contribution thanks to the relatively non-destructive, quantitative analysis. We present results on highly doped n and p type patterns on, respectively, p and n type silicon substrates. Using synchrotron radiation and spherical aberration-corrected energy filtering, we have obtained a spectroscopic image series at the Si 2p core level and across the valence band. Local band alignments are extracted, accounting for doping, band bending and surface photovoltage. (Some figures in this article are in colour only in the electronic version)

as a function of position within the microscope field of view (FoV). A full image series is a three-dimensional (3D) dataset I (x, y, E k ) allowing extraction of photoemission spectra from any area of interest (AOI) within the field of view. One particularly important application is the study of the electronic structure as a function of spatially dependent doping levels of silicon, whether in the form of doped patterns or gradients. Thus, whereas gate thicknesses are of the order of 1 nm, lateral device dimensions are closer to 100 nm. Although the dopant concentration is usually well below the PES detection levels, the effects on the band alignments should be readily measured. In particular, shifts in the Fermi level position as a function of doping, and band bending at the surface or at an interface, should be measurable. As Phaneuf et al [1] observed, this is a four-dimensional problem. Laterally, the electronic energy levels E are imaged as a function of position (x, y), including band bending across pn junctions, whereas perpendicular to the surface band bending has to be included as a function of z (whether this be due to the surface termination or to the presence of an oxide layer over the silicon substrate). Finally, there may also

1. Introduction The increasing integration of semiconductor devices makes the availability of reliable, quantitative, non-destructive analysis tools more and more important. Electron microscopy is well suited to the task in terms of spatial resolution. However, in order to obtain quantitative information on the chemistry and the electronic structure, the electron energies used must be reduced to a few hundred eV in order to privilege inplane surface and near surface contrast with respect to bulk heterogeneity. X-ray photoelectron emission microscopy (XPEEM) offers precisely the possibility to combine the required spatial and chemical state resolution. In particular, by using soft x-ray excitation combined with a full energy-filtered analysis, one may carry out XPEEM spectromicroscopy, combining the elemental, chemical and electronic structure sensitivities of classical photoelectron spectroscopy (PES) with spatial resolutions on the 100 nm scale, now easily accessible with current PEEM instruments. Image series as a function of photoelectron kinetic energy Ek are acquired step by step over the energy window of interest. Each image gives the intensity 0953-8984/09/314015+07$30.00

1

© 2009 IOP Publishing Ltd Printed in the UK

J. Phys.: Condens. Matter 21 (2009) 314015

N Barrett et al

Lens

Projection Lenses

MCP Screen Slits

Sample

CCD Camera Contrast Octopole Entrance Lens Aperture Stigmator System

Imaging Double Energy Analyser

Transfer Lens MCP Screen

(a)

(b)

Exit Lens System

CCD Camera

Figure 1. (a) Top: optical micrograph of doped patterns. Middle: N+ /P− sample. Bottom: P+ /N sample. Also shown: expected band line-ups in x – y (pn junction) and z (oxide/substrate interface). (b) Schema of the XPEEM instrument used showing the direct PEEM, selected-area XPS and energy-filtered PEEM modes. The double hemispherical analyser suppresses the α 2 aberrations inherent in a single hemispherical analyser.

spectromicroscopy. First the sample preparation and the XPEEM instrument used are described. Then we present the core level and valence band spectra extracted from regions of interest corresponding to different n and p type doping levels on the silicon wafers. The interpretation of the experimental results requires taking into account all of the contributions to the binding energies as measured by photoemission.

be unwanted additional effects such as surface contamination, either intrinsic to the wafers or as a result of x-ray irradiation during analysis, particularly when using undulator radiation at a synchrotron source. The first observation of contrast between p and n doped regions using electron microscopy was done by Chang and Nixon [2] using secondary electrons in a scanning electron microscope. In further studies by other groups, the basic rule was that p type areas were brighter than n type areas. This was attributed to the difference in band bending at the surface as a function of dopant type and concentration, and some sophisticated models have been developed [3]. However, the use of secondary electrons for imaging, or the use of UV excitation sources in PEEM experiments can make the extracted spectra extremely complex to disentangle. Frank et al [4] have recently reviewed the different contrast mechanisms which may play a role, including work function, band bending, electron–hole pair creation by hot electron absorption, direct transitions, surface contamination and spectral width of the photon source. Thus, the qualitative image contrast may be understood and related to the pn structures, but more quantitative analysis is extremely difficult. Furthermore, they did not benefit from full energy filtering. The image intensity thus represents integration over the band pass of the microscope, convoluted with the initial photon energy width. This has been partly overcome in PEEM experiments using a retarding energy filter [5]. Energy-filtered PEEM combined with a tuneable photon source such as synchrotron radiation can provide further information. It has already been used to study semiconductor surfaces, see for example [6, 7]. However, the most thorough study yet published [1] used a scanning photoelectron microscope to study variations in the electronic levels on a doped, patterned silicon wafer, thus combining lateral and energy resolution. Here we present the first thorough fully energy-filtered XPEEM study of a similar system, which benefits both from the insights obtained by Phaneuf et al and the instrumental improvements by using a PEEM instrument optimized for

2. Experimental details The samples were made in the Laboratoire d’Electronique et de Technologie de l’Information (LETI) at the CEA-Grenoble. The samples consisted of two-dimensional doped patterns implanted into silicon in the form of lines with variable spacing and width from 100 to 0.1 μm, see figure 1(a). Each set of lines was identified by figures with the same doping level, giving suitable shapes for optimization of the electron optics of the PEEM instrument. Two samples were studied, figure 1(a). The first sample, designated N+ /P− , had N+ doped zones (1020 cm−3 ) implanted into a P− substrate (1016 cm−3 ). The second, designated P+ /N, had P+ patterns (1020 cm−3 ) implanted into an N type (1017 cm−3 ) substrate; the latter was itself deposited on a Si P− wafer (1016 cm−3 ). A native oxide layer was present on both samples. Figure 1(a) also illustrates the four-dimensional problem of band line-ups in such samples. The spectromicroscopy experiments were done using a NanoESCA (Omicron Nanotechnology) [8] XPEEM instrument temporarily installed on the CIPO beamline of the ELETRRA synchrotron radiation source. A schema of the instrument is shown in figure 1(b). The NanoESCA has been specially designed to optimize spectral extraction in photoemission mode from small areas of interest. One major obstacle for most PEEM instruments is the transmission function. The transmission depends on the phase space acceptance of the instrument, which is in turn inversely proportional to the square of the pass energy when using a hemispherical-based energy analyser. Thus away from 2

J. Phys.: Condens. Matter 21 (2009) 314015

N Barrett et al

the photoemission threshold, the PEEM transmission sharply decreases, making imaging in photoemission mode difficult. Indeed, most spectroscopic PEEM work is done very efficiently by using the absorption mode at threshold and measuring the intensities as one sweeps through an absorption edge. The most systematic use of PEEM with full energy filtering is the work of Heun, Locatelli et al using a very bright photon source at the ELETTRA synchrotron, see for example [9, 10]. However, transmission remains a problem, and the energy resolution must often be relaxed to obtain good counting statistics [6]. The NanoESCA goes some way to overcoming this problem by an all electrostatic lens system and a low PEEM column voltage, close to the pass energy used in the energy analyser. Furthermore, the unique use of a double hemispherical analyser corrects the spherical α 2 aberrations inherent in a single hemisphere, where α is the entrance angle of the electrons in the analyser [8]. Thus one may use pass energies and energy analyser slits comparable to those used in standard XPS without overly sacrificing phase space and thus transmission. This can be at the expense of the ultimate lateral resolution, but the system does permit simultaneous XPEEM imaging of core and valence levels in reasonable acquisition times. The incident photon energy was 127 eV, representing the best compromise between the beamline undulator response and surface sensitivity. The PEEM contrast aperture diameter was 150 μm; a trade-off between lateral resolution and transmission. The double hemispherical analyser pass energy of the NanoESCA was 50 eV and 0.5 mm entrance slits were used. Image series through the Si 2p core level were acquired in 0.1 eV steps. The overall estimated energy resolution was 0.15 eV, with a lateral resolution of 120 nm. The incident photon flux on the sample was rather low for synchrotron-based PEEM experiments (∼1015 ph s−1 cm−2 ). The sample was close to ground potential, and an extraction voltage of 12 kV was used [11]. All results were taken using a 25 μm field of view. Image series as a function of the photoelectron kinetic energy were acquired for the Si 2p core level and for the valence band. The acquisition time per image for the former was 3 min, for the latter, 5 min. The photoelectron energy E is measured with respect to the sample Fermi level E F , thus E − E F = E k + WF , where E k is the photoelectron kinetic energy and WF the sample work function. The variation of the work function under undulator radiation was also measured, and will be detailed in a forthcoming paper. The maximum intrinsic energy dispersion in the vertical direction of the FoV is less than 35 meV and the binding energy scale was calibrated using the Fermi level and the 3d emission of a flat polycrystalline sputtered Ag sample with exactly the same energy filter settings as for the doped silicon.

(a)

(b)

(c)

(d)

Figure 2. (a) and (c) Threshold images of N+ /P− and P+ /N, respectively, using a 25 μm field of view; (b) and (d) Si 2p spectra averaged over the field of view of (a) and (c), showing broad peaks given the energy resolution. The threshold images have been obtained using high resolution 1 × 1 binning.

N+ (P+ ) regions on the P− (N) substrate for N+ /P− (P+ /N). The image series show clear contrast inversion for both samples, and will be analysed in a forthcoming paper. On the right of figure 2 we show the area-averaged Si 2p spectra acquired on N+ /P− and P+ /N using the NanoESCA in the XPS mode. In this mode the instrument functions as a spectrometer using only the first hemispherical analyser which projects the photoelectrons onto a channeltron detection system. The spectra have two main peaks, one due to the native oxide at a binding energy of 104 eV and another, strongly attenuated, from the underlying bulk Si substrate at 100 eV. The separation of the two peaks, about 4 eV, corresponds to what one would expect for oxidized silicon [12]. However, given the energy resolution (∼0.15 eV) the spectral features are too large to be attributed to single peaks. Thus it may well be that the averaging of the photoemission signal from doped and undoped regions gives a broad signal, hiding the spatially dependent band alignments. This is a first indication that there is mixing of the electronic levels in the same field of view. Figure 3 shows five images from the series of 91 images acquired through the Si 2p core level for the N+ /P− sample, with the corresponding binding energies (BE). This results in an image stack of the photoelectron intensity I (x, y, E k ). At high binding energy the contrast inversion over the Si4+ peak from the N+ and P− doped regions is clearly seen, indicating visually that the Si4+ peaks are shifted as a function of the doping type and concentration. There is a similar but much weaker inversion for the substrate peak. The small squares represent the areas of interest (AOIs) defined for spectral extraction (400 × 400 nm2 ). The resulting core level spectra are displayed in the bottom of figure 3 together with the best least square fits to the data. The colour code identifies the AOIs from which the spectra were extracted. Standard core level fitting criteria were applied to the extracted spectra. After subtraction of a Shirley background

3. Results and discussion 3.1. Si 2p core level imaging Figure 2 shows energy-filtered threshold images from the two samples. One can clearly distinguish the heavily doped 3

J. Phys.: Condens. Matter 21 (2009) 314015

N Barrett et al

Figure 3. Top: selected images from the energy-filtered image series through the Si 2p core level on sample N+ /P− with a field of view of 25 μm. The first image shows the 400 × 400 nm2 AOIs selected for extracting the local core level spectra. The contrast levels have been adjusted for better visibility. Bottom: core level spectra and best least square fits using standard literature parameters for Si 2p. The Si4+ component due to the native SiO2 oxide is in light grey, the sub-oxide components in grey and the Si0 substrate component in black. The modulation of the oxide thickness as a function of doping is clearly visible. The variation in the absolute intensity of the spectra is less than 5% across the different AOIs.

the oxide thickness difference z over N+ and P− regions, based on Himpsel et al’s figures, can be calculated to be 0.79 nm. Mean free path values of 0.5 and 0.35 nm give z equal to 0.54 and 0.38 nm, respectively. We have also performed spectroscopic imaging of N+ /P− using an optimized, monochromatic laboratory Al Kα source (hν = 1486.7 eV) [11]. At this energy λ = 2.96 nm, giving an average oxide thickness of 0.95 nm. Figure 4 shows selected images from the Si 2p series of the P+ /N sample, the definition of the AOIs and the extracted Si 2p spectra. In contrast to the N+ /P− spectra of figure 3, very little variation in the substrate Si0 signal is observed as a function of doping type. The two samples are not symmetric in their preparation. The N+ patterns of N+ /P− are obtained by implantation of phosphor into a P− substrate, whereas the P+ patterns of P+ /N are obtained by boron implantation into a phosphor implanted layer (N) on a boron (P− ) implanted substrate. The strain fields are thus different in the two cases and P+ /N has undergone a supplementary ion implantation to obtain the required doped patterns. Native oxide growth depends on the sample preparation history, it therefore seems reasonable that the oxide on P+ /N, having undergone successive ion implantations is more homogeneous than in N+ /P− .

function, a standard, five component deconvolution was applied, simulating the Si0 , Si sub-oxides and Si4+ components [13]. Gaussian line shapes with a 2p spin–orbit splitting of 0.61 eV and a 2:1 branching ratio were used. The full width half maxima used for the Si0 , Si+ , Si2+ , Si3+ and Si4+ were 0.6, 0.9, 1.0, 1.1 and 1.4 eV, respectively. The experimental intensities extracted from AOIs distributed horizontally across the FoV are remarkably constant; the root mean square deviation being less than 5%. The fits to the experimental spectra are very good. The ∼2 × 102 counts per binned pixel give a count rate from each AOI of ∼2 × 103 . The point χ 2 residual between the experimental data and the fit is 2.2 (∼0.1%) for spectra from the N+ regions and 3.0 for spectra from the P− regions. The standard deviation in the binding energy values obtained from spectra from different AOIs was 30 and 50 meV for the N+ and P− regions, respectively. Subtle changes occur in both the positions and the internal weightings of the Si 2p components. In particular, it is immediately obvious that the substrate signal is more strongly attenuated over the P− substrate than over the N+ pattern, indicating that the native oxide thickness is dependent on the underlying doping level and type. Using the core level intensities and applying a simple model of exponential attenuation of the substrate signal due to the finite electron inelastic mean free path λ [13] we can estimate the thickness of the oxide layer. Using the values of Himpsel et al [13] for the photoionization cross sections of Si0 and Si4+ at hν = 130 eV and the mean free path of the Si 2p electrons (0.75 nm) the N+ (P− ) oxide thickness is 1.81 (2.60) nm. A smaller mean free path of 0.5 nm gives oxide thicknesses of 1.36 (1.90) nm respectively, and setting λSi = λSiO2 = 0.35 nm gives 1.07 (1.45) nm. It has been shown that for low E k , the elastic component of the mean free path becomes significant due to scattering from final state band gaps [14]. Thus, the absolute value of the oxide overlayer thickness is uncertain. However,

3.2. Valence band imaging Image series were also acquired near the top of the valence band up to the Fermi level. The extracted spectra for N+ /P− and P+ /N are shown in figure 5 with, for convenience, a reminder of the AOIs used. The Fermi level is marked by a dotted line. Two main features are visible in all spectra. Firstly, the O 2p orbitals which as expected peaked at 6–7 eV below the Fermi level, secondly, a small but significant contribution from the Si 3p orbitals, which comes from the underlying substrate. The Si 3p valence band contribution is attenuated 4

J. Phys.: Condens. Matter 21 (2009) 314015

N Barrett et al

Figure 4. Top: selected binding energy images from the energy-filtered image series through the Si 2p core level on sample P+ /N with a field of view of 25 μm. Contrast inversion through the Si0 substrate peak is clearly visible. The second image shows the 400 × 400 nm2 AOIs selected for extracting the local core level spectra. Bottom: core level spectra and best least square fits using standard literature parameters for Si 2p. The colour code corresponds to the AOIs defined on the second image. No modulation of the oxide thickness as a function of doping is visible.

Table 1. Si 2p substrate binding energy, Si0 /Si4+ core level shift, O 2p and Si 3p valence band onsets measured from the doped patterns and substrates of samples N+ /P− and P+ /N. All energies are in eV. N+ /P− +

N

P

P+ /N



P

Si 99.34 ± 0.03 99.60 ± 0.05 Si4+ 4.02 ± 0.03 3.68 ± 0.05 VBM O 2p 4.98 4.79 VBM Si 3p — — 0

(a)

+

99.52 ± 0.05 4.06 ± 0.05 5.12 0.54

N 99.59 ± 0.03 3.95 ± 0.03 5.00 0.44

the band bending between the substrate and the native oxide will extend over several nm, approximately 8 L D , even for the most heavily doped patterns. Given the small photoelectron inelastic mean free path (∼0.35–0.75 nm, see above), this means that the valence band maximum (VBM) measured from our extracted spectra will indeed measure the onsets for the fully bent bands, and that we are far from the flat band regime. In fact, thanks to the use of tuneable synchrotron radiation, we are able to probe the spatial distribution of band bending at the buried substrate/oxide interface. The core level and valence band maximum results for the two samples are summarized in table 1.

(b)

Figure 5. Top of the valence band spectra extracted from the same areas of interest as for the Si 2p core level spectra of figures 3 and 4. (a) N+ /P− . (b) P+ /N. The densities of states due to the O 2p and Si 3p orbitals are marked, together with examples of linear extrapolation in order to determine the valence band onsets. The threshold images with the relevant AOIs are reproduced for convenience.

3.3. Band bending The binding energy of a core electron in a doped semiconductor as measured by photoemission using an intense x-ray source can be written as: doping

BE = BEifb + E F

by the native oxide, but is still visible. As for the Si 2p spectra, the attenuation is stronger in the spectra extracted from the p doped region than in those extracted from the n type pattern. Extrapolating the upper edges of the O 2p and the Si 3p to zero allows a first determination of the  valence band onsets. The Debye length is given by L D = ε S kT /q 2 N [16], thus

+ E BB + E SPV ,

(1)

where BEifb the binding energy is measured in the intrinsic case doping is the shift in the position and in flat band conditions; E F of the Fermi level within the gap as a function of doping with respect to intrinsic silicon; E BB is the band bending at the 5

J. Phys.: Condens. Matter 21 (2009) 314015

N Barrett et al

Figure 6. (a) Schema showing how doping, band bending and surface photovoltage interact to modify the electronic energy levels in N+ zones of N+ /P− with respect to the values obtained for intrinsic silicon. The dotted lines represent intrinsic silicon; the dashed line is the position of the Fermi level in the heavily doped region. (b) Scale drawing of results for the N+ region in N+ /P− , with the calculated SPV effect.

Table 3. The estimated band bending at the oxide/substrate interface from the Si 2p analysis, corrected for the SPV effect.

Table 2. Calculated surface photovoltage effect following Hecht [17]. Doping level (cm−3 ) 1017 1020

E SPV (eV)

Pattern type N+ N P+ P−

−0.4 −0.2

substrate/oxide interface; and E SPV is the binding energy shift due to the surface photovoltage (SPV). Given the available photon energy range of the beamline and thus the inelastic mean free path, it was not possible to access the flat band region using synchrotron radiation. However, the binding energy for nearly intrinsic silicon is doping can be well-known and taken to be 99.35 eV [15]. E F calculated using ND = n i exp((E F − E i )/kT ) [16]. With synchrotron radiation, the high intensity induces a significant surface photovoltage caused by the creation of hole– electron pairs by the incoming photons. The local field caused by the upwards band bending (in the case of n type doping) at the substrate/oxide interface sweeps electrons into the bulk of the substrate and attracts holes in the valence band towards the interface. Thus the surface photovoltage acts to counter the band bending. In the case of p type doping the field is reversed, but the SPV acts again to ‘flatten’ the bands. The SPV can be calculated as [17]:

Band bending (eV)

−0.8 −0.6 +0.5 +0.2

The results for the N+ region are shown in figure 6(b) showing both core level and valence band binding energies. For N+ /P− the measured binding energy is 99.3 eV in the heavily n doped region, and 99.60 eV in the p doped substrate. As can be judged from equation (1), these values are the result of several contributions, and failure to take into account the different terms on the right-hand-side of equation (1) would inevitably result in a wrong interpretation of the band alignments. The effect of heavy n doping shifts the position of the Fermi level in the gap. With the low escape depth of the 2p electrons stimulated by the 127 eV incident photons, this is countered by the upwards band bending, which is itself partially flattened by the x-ray induced surface photovoltage. From the SPV values we can therefore deduce the real band bending at the oxide/substrate interface as a function of substrate doping. The results are summarized in table 3 for N+ /P− and P+ /N. The spectroscopic imaging of N+ /P− using a monochromatic Al Kα source gives an inelastic mean free path of ∼3 nm, making topmost surface effects negligible, whilst probing deeper into the substrate. The threshold image is shown in figure 7. Although not carried out in situ, the results are valuable in checking the SPV calculation. The Si0 binding energies determined using Al Kα radiation are 99.1 eV (N+ ) and 99.8 eV (P− ). In the case of the N+ region this is just the value of the SPV, which is indeed expected to be much smaller, or even negligible with a laboratory source, compared to synchrotron radiation. In the limit of low flux, the SPV term

J = Jmax (1 − exp(−αW )) ≈ J0 (T ) exp (−E CBO /E 0 ) . The generated photocurrent J is a function of the incoming flux, the photon absorption coefficient, the thermionic emission properties of the sample and the electron effective mass. We have calculated the E SPV for the CIPO flux of 1015 ph s−1 cm−2 as shown in table 2. Thus the SPV, with the photon flux used on the CIPO beamline and the doping levels of the patterns and substrate, is far from being negligible, and can be of the same order of magnitude as the Fermi level shifts expected from the dopant concentration. The interaction of doping, band bending and surface photovoltage is shown in figure 6(a). 6

J. Phys.: Condens. Matter 21 (2009) 314015

N Barrett et al

study variations in electronic band alignments at the native oxide/substrate interface as a function of p and n type doping in micron sized patterns on silicon wafers. High quality Si 2p spectra with good energy resolution (0.15–0.2 eV) are extracted from 400 × 400 nm2 areas of interest and correlated with the valence band spectra from the same regions. Calculation of the surface photovoltage induced by the synchrotron radiation allows a direct estimate of the real band bending at the interface as a function of substrate doping. The results open perspectives for the study of multiple doping levels and doping gradients in silicon and other semiconductors and point to the use of energy-filtered XPEEM for non-destructive, but still offline, characterization of microelectronic devices.

Figure 7. Threshold image obtained in laboratory conditions using an Al Kα source and E − E F = 6.1 eV. The FoV is 127 μm, and the acquisition time 8 s. The N+ patterns are dark in the image.

Acknowledgments We thank the CIPO beamline scientists Nicola Zema and Stefano Turchini for their valuable help. This work was supported by the French ANR project 05-NANO-065 XPEEM.

in equation (1) is set to zero, thus the band bending as measured at the interface is simply equivalent in magnitude to the shift of the Fermi level due to doping. The values given in table 3 are doping indeed within 20% of the shifts expected from E F . Confirmation of the band bending at the substrate/oxide interface comes from the separation Si4+ between the Si0 and the Si4+ components in the n and p type doped zones, clearly showing the effect of the opposite band bending expected for the two dopants, modulated of course by the SPV. Thus, it is possible to deduce the spatial distribution of real band bending at the interface, free of effects induced by the photoemission analysis. The O 2p bands of the SiO2 native oxide are not bent; however, their alignment does follow the substrate valence bands. Thus the measured valence band onset for the O 2p levels reflects the combined effect of doping, shifting the Fermi level position in the gap and the substrate band bending. Thus the difference in valence band line-up is smaller than that expected from a flat band regime. The VBM of the Si 3p orbitals is not computed due to the low counting statistics extracted from the image series. In the case of P+ /N, the statistics are better and the Si0 , 4+ Si binding energies can be quantified, as well as the valence band onsets of the O 2p and even the Si 3p orbitals. We recall that in the extracted Si 2p spectra in figures 3 and 4 the substrate signal was considerably sharper and more intense for P+ /N than for N+ /P− . Most notable is the proximity of the measured binding energies in the n and p type regions, underlying the need for using quantitatively equation (1) in the interpretation of the experimental spectra. The Si0 binding energy measured from the 400 × 400 nm2 AOIs can therefore be used to calculate the real band bending at the substrate/oxide interface as a function of doping type and level.

References [1] Phaneuf R J, Kan H-C, Marsi M, Gregoratti L, G¨unther S and Kiskinova M 2000 J. Appl. Phys. 88 863 [2] Chang T H P and Nixon W C 1967 Solid-State Electron. 10 702 [3] Ballarotto V W, Siegrist K, Phaneuf R J and Williams E D 2002 J. Appl. Phys. 91 469 [4] Frank L, Mika F, Hovorka M, Valdaitsev D, Schoenhense G and Mullerova I 2007 Mater. Trans. 48 936 [5] Frank L, Mullerova I, Valdaitsev D A, Gloskovskii A, Nepijko S A, Elmers H-J and Schoenhense G 2006 J. Appl. Phys. 100 093712 [6] Heun S, Kremmer S, Ercolani D, Wurmbauer H and Teichert C 2005 J. Electron Spectrosc. Relat. Phenom. 144–147 1163 [7] Charlier J, Palacin S, Leroy J, Del Frari D, Zagonel L F, Barrett N, Renault O, Bailly A and Mariolle D 2008 J. Mater. Chem. 18 3136 [8] Escher M, Weber N, Merkel M, Ziethen C, Bernhard P, Sch¨onhense G, Schmidt S, Forster F, Reinert F, Kr¨omker B and Funnemann D 2005 J. Phys.: Condens. Matter 17 S1329 [9] Biasiol G, Heun S, Golinelli G B, Locatelli A, Mentes T O, Guo F Z, Hofer C, Teichert C and Sorba L 2005 Appl. Phys. Lett. 87 223106 [10] Mori G, Lazzarino M, Ercolani D, Biasiol G, Locatelli A, Sorba L and Heun S 2006 Nucl. Instrum. Methods B 246 39 [11] Renault O, Barrett N, Bailly A, Zagonel L F, Mariolle D, Cezar J C, Brookes N B, Winkler K, Kromker B and Funnemann D 2007 Surf. Sci. 601 4727 [12] Hollinger G and Himpsel F J 1984 Appl. Phys. Lett. 44 93 [13] Himpsel F J, McFeely F R, Taleb-Ibrahimi A, Yarmoff J A and Hollinger G 1988 Phys. Rev. B 38 6084 [14] Barrett N, Themlin J-M, Krasovskii E E and Strocov V N 2005 Phys. Rev. B 71 035427 [15] Renault O, Barrett N, Samour D and Quiais-Marthon S 2004 Surf. Sci. 566 526 [16] Sze S M and Ng Kwok K 2007 Physics of Semiconductor Devices (New Jersey: Wiley) p 85 [17] Hecht M H 1990 Phys. Rev. B 41 7981 Alonso M, Cimino R and Horn K 1990 Phys. Rev. Lett. 64 1947

4. Conclusion We have used fully energy-filtered x-ray photoelectron emission microscopy and synchrotron radiation in order to

7

Spatially resolved, energy-filtered imaging of core level ...

Jul 7, 2009 - CCD Camera. Figure 1. (a) Top: optical micrograph of doped patterns. ..... The point χ2 residual between the experimental data and the fit is 2.2 ...

1MB Sizes 1 Downloads 135 Views

Recommend Documents

Spatially Resolved Mapping of Polarization Switching ...
Apr 5, 2007 - memories,[1] data storage,[2] resistive memories,[3] multiferroic devices with ... characterization of ferroelectricity in confined systems. Roe-.

Spatially Resolved Quantum Nano-Optics of Single ...
Apr 9, 2013 - quantum states generation in an electron microscope, and show that it clearly makes ... Thus, generally an SPS will have a limited size: an atom.

Download Musculoskeletal Imaging: A Core Review ...
offering tablet, smartphone, or online access to:Complete content with enhanced. navigationA powerful search that pulls results from content in the book, your ... textAbility to take and share notes with friends and. colleaguesQuick reference tabbing

MULTICRITERIA MAINTENANCE PROBLEM RESOLVED BY ... - DIT
1 if replacement is realized between missions k and k + 1,. 0 otherwise. Total time TMR(k) and total cost CMR(k) nec- essary to minimal repairs are given by:.

Angle-resolved and resonant photoemission ...
did not use the second derivative method to map out the band .... electronlike band in the band mapping. .... graphic Data for Intermetallic Phases, 2nd ed.

Supplementary Information: Quantitative, time-resolved measurement ...
Martin Hegner, CRANN, School of Physics, Trinity College Dublin,. Ireland; [email protected] ... This commoving mass is also called 'virtual mass'. Second, an.

MULTICRITERIA MAINTENANCE PROBLEM RESOLVED BY ... - DIT
management, not always obvious, of weight sets, but also a ... with breaks of known length between each mis- ... the functioning probability of a system for a mis-.